Vijay Laxmi Impex is a reputed Hardened and tempered Steel Strips manufacturer, supplier, and exporter in India. We give you options for the thickness, width, and length of your Hardened and tempered steel strips and can also adjust the size to exactly what you need. For each batch, chemical, mechanical, surface, and dimensional tests are carried out to guarantee durability and performance.
Vijay Laxmi Impex is an eminent Hardened And Tempered Steel Strips supplier in India. We use the latest manufacturing technology and modern equipment as an ISO-certified company to manufacture top-performing Hardened and tempered Rolled Steel Strip. High-quality raw materials are used for our products, and they are heated and forged in a controlled way to achieve great strength, hardness, and flexibility.
| Specification of Hardened and tempered | |
| Thickness (mm) | 0.05 – 3.5mm & above |
| Full Width Range (mm) | 550 Max |
| Slit Width (mm) | 2.5mm to 550mm |
| Finish | Grey, Bright, Blue, Bronze |
| Edges | Slit, Mill, Square, and, Round Edges |
| Standards | AISI, ASTM, BS, DIN, GB |
|
SPECIFICATIONS |
THICKNESS (mm) |
WIDTH (mm) |
|
C-50, 55C6, C-60, 65C6, 70C6, 75C6, 80C6, 85C6, 98C6, 50CrV4, |
0.20-0.50 |
30-250 |
|
0.50-1.00 |
20-350 |
|
|
1.00-2.00 |
10-400 |
|
|
2.00-4.00 |
15-400 |
|
MECHANICAL PROPERTIES |
||
|
GRADE |
HARDENED & TEMPERED |
|
|
HARDNESS (HV) |
U.T.S. (N/mm2) |
|
|
C-55, C-62, C-65, C-75, C-80, C-85, |
280-320 |
900-1030 |
|
320-350 |
1030-1130 |
|
|
350-380 |
1130-1220 |
|
|
380-420 |
1220-1350 |
|
|
420-450 |
1350-1460 |
|
|
450-480 |
1460-1560 |
|
|
480-520 |
1560-1700 |
|
|
520-550 |
1700-1810 |
|
|
THICK./WIDTH |
FOR THICKNESS |
FOR WIDTH |
||||||
|
UPTO 100 |
100-200 |
ABOVE 200 |
UPTO 100 |
100-200 |
ABOVE 200 |
|||
| SLIT EDGE | DRESSED EDGE | SLIT EDGE | DRESSED EDGE | SLIT EDGE | ||||
| 0.15-0.25 | ±0.015 | ±0.015 | ±0.020 | ±0.20 | – | ±0.20 | – | ±0.30 |
| 0.25-0.40 | ±0.020 | ±0.020 | ±0.025 | ±0.20 | ±0.15 | ±0.20 | ±0.15 | ±0.30 |
| 0.40-0.60 | ±0.020 | ±0.020 | ±0.030 | ±0.20 | ±0.10 | ±0.20 | ±0.15 | ±0.30 |
| 0.60-0.90 | ±0.025 | ±0.025 | ±0.030 | ±0.20 | ±0.10 | ±0.20 | ±0.20 | ±0.30 |
| 0.90-1.20 | ±0.030 | ±0.030 | ±0.030 | ±0.20 | ±0.15 | ±0.25 | ±0.20 | ±0.40 |
| 1.20-1.60 | ±0.030 | ±0.030 | ±0.035 | ±0.20 | ±0.15 | ±0.25 | ±0.25 | ±0.40 |
|
S.No.
|
Indian Steel Grade
|
Equivalent International Steel Grades
|
Chemical Composition Specifications
|
|||||||||||||
|
American
|
European
|
England
|
Germany
|
Japanese
|
||||||||||||
|
IS
|
SAE
|
EN
|
BS
|
DIN
|
JIS
|
C%
|
Mn%
|
Si%
|
P%
|
S%
|
Cr%
|
Cu%
|
Ni%
|
V%
|
Others%
|
|
| 1 | C 40 | SAE 1040 | C 40 | EN 8 | C 40 | S40C | 0.35 – 0.45 | 0.60 – 0.90 | 0.15 – 0.35 | 0.040 max. | 0.040 max. | – | – | – | – | – |
| 2 | 45C8 | SAE 1045 | C 45 | – | C 45 | S45C | 0.40 – 0.50 | 0.60 – 0.90 | 0.10 – 0.35 | 0.050 max. | 0.050 max. | – | – | – | – | – |
| 3 | – | SAE 1050 | C 50 | EN 43 | C 50 | S50C | 0.47 – 0.55 | 0.60 – 0.90 | 0.10 – 0.35 | 0.045 max. | 0.045 max. | 0.40 max | – | 0.40 max. | – | Mo – 0.10max. |
| 4 | 55C6 | SAE 1055 | C55S | EN 9 | C 55 | S55C | 0.50 – 0.60 | 0.60 – 0.90 | 0.10 – 0.35 | 0.050 max. | 0.050 max. | – | – | – | – | – |
| 5 | – | SAE 1060 | C60S | – | C 60 | S60C | 0.57 – 0.65 | 0.60 – 0.90 | 0.10 – 0.35 | 0.045 max. | 0.045 max. | 0.40 max | – | 0.40 max. | Mo – 0.10 max. | |
| 6 | 65C6 | SAE 1065 | – | EN 42B | C 62 | S65C | 0.60 – 0.70 | 0.50 – 0.80 | 0.10 – 0.35 | 0.050 max. | 0.050 max. | – | – | – | – | – |
| 7 | 70C6 | SAE 1070 | C67S | – | C 67 | S70C | 0.65 – 0.75 | 0.50 – 0.80 | 0.10 – 0.35 | 0.050 max. | 0.050 max. | – | – | – | – | – |
| 8 | 75C6 | SAE 1075 | C75S | EN 42C | C 75 | – | 0.70 – 0.80 | 0.50 – 0.80 | 0.10 – 0.35 | 0.050 max. | 0.050 max. | – | – | – | – | – |
| 9 | C75-Cr25 | – | – | – | – | – | 0.70 – 0.78 | 0.60-0.80 | 0.35 max | 0.035 max | 0.030 max. | 0.15 – 0.27 | – | – | – | AI – 0.010 – 0.040 |
| 10 | – | – | – | – | 75Cr1 | – | 0.70 – 0.80 | 0.60 – 0.80 | 0.25 – 0.50 | 0.030 max | 0.030 max. | 0.30 – 0.40 | – | – | – | – |
| 11 | 80C6 | SAE 1080 | – | EN 42J | C 80 | – | 0.75 – 0.85 | 0.50 – 0.80 | 0.10 – 0.35 | 0.050 max. | 0.050 max. | – | – | – | – | – |
| 12 | 85C6 | SAE 1085 | – | EN 42D | – | – | 0.80 – 0.90 | 0.50 – 0.80 | 0.10 – 0.35 | 0.050 max. | 0.050 max. | – | – | – | – | – |
| 13 | – | SAE-1086 | C85S | – | – | SK85 | 0.80-0.90 | 0.50 max. | 0.35 max. | 0.030 max | 0.030 max | 0.30 max. | 0.25 max | 0.25 max | – | – |
| 14 | – | SAE-1095 | C100S | EN 44D | CK 101 | SK95 | 0.90-1.00 | 0.50 max. | 0.35 max. | 0.030 max | 0.030 max | 0.30 max. | 0.25 max | 0.25 max | – | – |
| 15 | 50Cr4V2 | SAE 6150 | 51CrV4 | EN 47 | 50CrV4 | SUP10 | 0.47 – 0.55 | 0.70 – 1.10 | 0.15 – 0.35 | 0.040 max. | 0.040 max. | 0.90 – 1.20 | – | – | 0.10 – 0.20 | – |
| 16 | – | – | – | – | 58CrV4 | – | 0.55 – 0.62 | 0.70 – 1.10 | 0.10 – 0.40 | 0.035 max. | 0.035 max. | 0.90 – 1.20 | – | – | 0.10 – 0.20 | – |
| 17 | – | – | C120U | – | – | SK120 |
1.15 – 1.25 |
0.10 – 0.50 | 0.10- 0.35 | 0.030 max. | 0.030 max. | – | – | – | – | – |
| 18 | – | – | 125Cr2 | – | – | SKS 81 |
1.10 – 1.30 |
0.50 max. | 0.35 max. | 0.030 max. | 0.030 max. | 020 – 0.50. | – | – | – | – |
|
Vickers Hardness HV |
Rockwell Hardness
|
Tensile Strength N/mm² (kgf/mm² ) |
Vickers Hardness HV |
Rockwell Hardness
|
Tensile Strength N/mm² (kgf/mm² ) |
Vickers Hardness HV |
Rockwell Hardness
|
Tensile Strength N/mm² (kgf/mm² ) |
|||
|
B Scale HRB |
C Scale HRC |
B Scale HRB |
C Scale HRC |
B Scale HRB |
C Scale HRC |
||||||
|
940
|
–
|
68.0
|
–
|
540
|
–
|
51.7
|
1860 (190)
|
280
|
(103.5)
|
27.1
|
890 (91)
|
|
920
|
–
|
67.5
|
–
|
530
|
–
|
51.1
|
1825 (186)
|
275
|
–
|
26.4
|
875 (89)
|
|
900
|
–
|
67.0
|
–
|
520
|
–
|
50.5
|
1795 (183)
|
270
|
(102.0)
|
25.6
|
855 (87)
|
|
880
|
–
|
66.4
|
–
|
510
|
–
|
49.8
|
1750 (179)
|
265
|
–
|
24.8
|
840 (86)
|
|
860
|
–
|
65.9
|
–
|
500
|
–
|
49.1
|
1705 (174)
|
260
|
(101.0)
|
24.0
|
825 (84)
|
|
840
|
–
|
65.3
|
–
|
490
|
–
|
48.4
|
1660 (169)
|
255
|
–
|
23.1
|
805 (82)
|
|
820
|
–
|
64.7
|
–
|
480
|
–
|
47.7
|
1620 (165)
|
250
|
99.5
|
22.2
|
795 (81)
|
|
800
|
–
|
64.0
|
–
|
470
|
–
|
46.9
|
1570 (160)
|
245
|
–
|
21.3
|
780 (79)
|
|
780
|
–
|
63.3
|
–
|
460
|
–
|
46.1
|
1530 (156)
|
240
|
98.1
|
20.3
|
765 (78)
|
|
760
|
–
|
62.5
|
–
|
450
|
–
|
45.3
|
1495 (153)
|
230
|
96.7
|
(18.0)
|
730 (75)
|
|
740
|
–
|
61.8
|
–
|
440
|
–
|
44.5
|
1460 (149)
|
220
|
95.0
|
(15.7)
|
695 (71)
|
|
720
|
–
|
61.0
|
–
|
430
|
–
|
43.6
|
1410 (144)
|
210
|
93.4
|
(13.4)
|
670 (68)
|
|
700
|
–
|
60.1
|
–
|
420
|
–
|
42.7
|
1370 (140)
|
200
|
91.5
|
(11.0)
|
635 (65)
|
|
690
|
–
|
59.7
|
–
|
410
|
–
|
41.8
|
1330 (136)
|
190
|
89.5
|
(8.5)
|
605 (62)
|
|
680
|
–
|
59.2
|
–
|
400
|
–
|
40.8
|
1290 (131)
|
180
|
87.1
|
(6.0)
|
580 (59)
|
|
670
|
–
|
58.8
|
–
|
390
|
–
|
39.8
|
1240 (127)
|
170
|
85.0
|
(3.0)
|
545 (56)
|
|
660
|
–
|
58.3
|
–
|
380
|
(110.0)
|
38.8
|
1205 (123)
|
160
|
81.7
|
(0.0)
|
510 (53)
|
|
650
|
–
|
57.8
|
–
|
370
|
–
|
37.7
|
1170 (120)
|
150
|
78.7
|
–
|
490 (50)
|
|
640
|
–
|
57.3
|
–
|
360
|
(109.0)
|
36.6
|
1130 (115)
|
140
|
75.0
|
–
|
455 (46)
|
|
630
|
–
|
56.8
|
–
|
350
|
–
|
35.5
|
1095 (112)
|
130
|
71.2
|
–
|
425 (44)
|
|
620
|
–
|
56.3
|
–
|
340
|
(108.0)
|
34.4
|
1070 (109)
|
120
|
66.7
|
–
|
390 (40)
|
|
610
|
–
|
55.7
|
–
|
330
|
–
|
33.3
|
1035 (105)
|
110
|
62.3
|
–
|
–
|
|
600
|
–
|
55.2
|
–
|
320
|
(107.0)
|
32.2
|
1005 (103)
|
100
|
56.2
|
–
|
–
|
|
590
|
–
|
54.7
|
2055 (210)
|
310
|
–
|
31.0
|
980 (100)
|
95
|
52.0
|
–
|
–
|
|
580
|
–
|
54.1
|
2020 (206)
|
300
|
(105.5)
|
29.8
|
950 (97)
|
90
|
48.0
|
–
|
–
|
|
570
|
–
|
53.6
|
1985 (202)
|
295
|
–
|
29.2
|
935 (96)
|
85
|
41.0
|
–
|
–
|
|
560
|
53.0
|
1950 (199)
|
290
|
(104.5)
|
28.5
|
915 (94)
|
|||||
|
550
|
52.3
|
1905 (194)
|
285
|
–
|
27.8
|
905 (92)
|
|||||
| Annealed | Hardened & Tempered | |||||||||
| Sr.No. | Grade | Vickers Hardness HV, Max. |
Yield Stress N/mm2,Min. |
Tensile Strength N/mm2,Max. |
Elongation, Percent ,Min. |
Vickers Hardness HV Min-Max. | Yield tress N/mm2, Min. |
Tensile Strength N/mm2, Max. |
Elongation, Percent, Min., Guage Length 5.65 |
|
| 1 | 45C 8 | 185 | » | 270 | 590 | 30 | 350 to 425 | 1030 | 1180 to 1420 | 6 |
| 2 | 55C 6 | 195 | ||||||||
| 3 | 65C 6 | 205 | ||||||||
| 4 | 70C 6 | 215 | ||||||||
| 5 | 75C 6 | 220 | » |
290
|
640 | 25 | 350 to 475 | 1080 | 1180 to 1570 | 6 |
| 6 | 80C 6 | 220 | ||||||||
| 7 | 85C 6 | 220 | ||||||||
| 8 | 98C 6 | 225 | 310 | 690 | 25 | 475 to 540 | 1470 | 1570 to 1760 | 6 | |
| 9 | 55Si7 | 240 | 340 | 780 | 20 | 475 to 570 | 1470 | 1570 to 1960 | 6 | |
| 10 | 50Cr4 | 240 | 340 | 780 | 20 | 505 to 650 | 1570 | 1670 to 2260 | 5 | |
| 11 | 50Cr4V2 | 240 | 340 | 780 | 20 | 555 to 670 | 1760 | 1880 to 2360 | 4 | |
| ITEM | END USE | APPLICATIONS |
| CUTTING SAW | BANDSAW | WOODCUTTING |
| GANGSAW | MARBLE CUTTING | |
| CIRCULAR SAW | WOOD/MARBLE | |
| BACKSAW | WOODCUTTING | |
| PIT SAW/ HANDSAW /CROSS-CUT | WOOD CUTTING | |
| AUTOMOTIVE SECTOR | AUTOMOTIVE COMPONENT | CIRCLIPS, WASHERS, SPRINGS & RECLINER |
| CLUTCH ASSEMBLY | ||
| DISC WASHERS | ||
| DISC PLATE | ||
| DRIVEN PLATE | ||
| GARDENING TOOLS/AGRICULTURE | CUTTING OPERATION | HARVESTING |
| HECKSAW BLADE | ||
| GARDENING TOOLS | ||
| MASONRY TOOLS | TROWEL/KARNI | BRICK LAYING |
| SQUARE TROWEL | WALL PLANER | |
| WALL PUTTY | WALL PAINTING | |
| SURGICAL BLADE | DOCTOR BLADE | MEDICAL OPERATION |
| STATIONERY | STAPLER | PAPER WORK |
| SHARPENER BLADE | SHAPENING PENCILS | |
| MEASURING DEVICE | MEASURING TAPE | CARPENTRY, CIVIL & MECHANICAL FIELD |
| SPRINGS | INDUSTRIAL STRIP SPRINGS | AUTOMOTIVES & ENGG. INDUSTRIES |
| SHUTTER SPRINGS | ||
| OTHERS | SHAVING BLADE | SHAVING |
| SUGARCANE KNIFE | SUGARCANE HARVESTING | |
| DOCTOR BLADE | PAPER INDUSTRIES & PRINTING PRESS |